Carbon Graphite |
| |
| Category |
Model |
Density
g/cm3 |
Bending
Strength
Mpa |
Compression
Strength
Mpa |
Shaw
Hardness
HS |
Porosity
% |
Impregnated Epoxy
Resin(H) |
M106H |
1.75 |
65 |
200 |
85 |
2.5 |
| M120H |
1.70 |
60 |
180 |
80 |
2.5 |
| M205H |
1.70 |
60 |
200 |
70 |
2.5 |
| M252H |
1.72 |
45 |
120 |
45 |
2.5 |
Impregnated Furan
Resin(K) |
M106K |
1.75 |
67 |
200 |
90 |
2.0 |
| M120K |
1.70 |
62 |
180 |
85 |
2.0 |
| M205K |
1.70 |
62 |
180 |
75 |
2.0 |
| M252K |
1.72 |
47 |
120 |
48 |
2.0 |
| KC-170 |
1.82 |
68 |
200 |
80 |
2.0 |
Impregnated Phenol
A 1dehyde Resin(F) |
M106F |
1.75 |
60 |
200 |
85 |
2.0 |
| M120F |
1.70 |
55 |
180 |
80 |
2.0 |
| M205F |
1.70 |
55 |
200 |
70 |
2.0 |
| M252F |
1.72 |
40 |
120 |
45 |
2.0 |
| KC-573 |
1.85 |
85 |
370 |
110 |
2.0 |
| KC-673 |
1.87 |
78 |
245 |
87 |
2.0 |
|
| |
Hot-pressed Graphite Technique Parameter |
| |
| Volume Density |
1.68g/cm3 |
| Shaw Hardness |
65-80HS |
| Compression Strength |
147Mpa |
| Bend Strength |
54Mpa |
| Frictional Factor |
0.15mm |
| Indicated Porosity |
0.3% |
|